* eSUN HIPS, 3 mm: Lower first layer bed temp to 100HEADmasterPatrick McDermott2019-10-211-2/+2
|
* PCIe MC Bracket: Decrease some extrusion widthsPatrick McDermott2019-10-211-4/+4
|
* PCIe MC Bracket: Increase extrusion widthsPatrick McDermott2019-10-211-8/+8
|
* PCIe MC Bracket: Slow bridges to 20 mm/sPatrick McDermott2019-10-211-2/+2
|
* TAZ 6, SE v2.1, eSUN HIPS: Retract 2 mmPatrick McDermott2019-10-211-2/+2
|
* TAZ 6, SE v2.1: Retract more before lifting at endPatrick McDermott2019-10-213-4/+4
| | | | Hopefully this will reduce stringing at the end.
* PCIe MC Bracket: New print preset copied from BasePatrick McDermott2019-10-212-1/+87
| | | | And switch to it.
* Base: Slow perimeters to 30 mm/sPatrick McDermott2019-10-211-4/+4
| | | | | This reduces corner seam blobs/zits/bumps/bulges/swell, at a cost of 19 seconds added print time for one PCI Express Mini Card bracket.
* Base: Slow perimeters and bridges to 40 mm/sPatrick McDermott2019-10-201-5/+5
|
* Base: Slow down on outer surfacesPatrick McDermott2019-10-201-7/+7
|
* Base; Increase speedsPatrick McDermott2019-10-201-10/+10
|
* Revert "eSUN HIPS, 3 mm: Cool bed to 90 after first layer"Patrick McDermott2019-10-201-2/+2
| | | | | | This reverts commit 0ab47538d6f7795ec468e04afa587205aba48942. Slight warping.
* Revert "eSUN HIPS, 3 mm: Lower first layer bed temp to 100"Patrick McDermott2019-10-201-2/+2
| | | | | | This reverts commit 350dad21ed236c603e9a9c24899523c92cad44d0. Warping, as expected.
* eSUN HIPS, 3 mm: Lower first layer bed temp to 100Patrick McDermott2019-10-201-2/+2
|
* eSUN HIPS, 3 mm: Cool bed to 90 after first layerPatrick McDermott2019-10-201-2/+2
|
* eSUN HIPS: Increase removal bed temp to 80Patrick McDermott2019-10-203-3/+3
|
* eSUN HIPS, 3 mm: Cool bed to 100 after first layerPatrick McDermott2019-10-201-2/+2
|
* eSUN HIPS, 3 mm: Increase bed temps to 110Patrick McDermott2019-10-201-3/+3
| | | | Trying to reduce warping.
* Revert "Revert "eSUN HIPS, 3 mm: Unlimit fan speed (again)""Patrick McDermott2019-10-201-2/+2
| | | | | | This reverts commit 4608b1f4bca70d80504a539d3709fc1e42934cc6. A bridge support failed.
* Revert "eSUN HIPS, 3 mm: Unlimit fan speed (again)"Patrick McDermott2019-10-191-2/+2
| | | | This reverts commit a1e55d2d6ecd91eceb6415a052e32106443cddcd.
* Revert "Base: Lay infill before perimeters"Patrick McDermott2019-10-191-2/+2
| | | | | | This reverts commit 3d5e961c51b9391fb45453122a40b4687f60bed5. Slic3r tries to start the infill from mid-air in some areas.
* Base: Lay infill before perimetersPatrick McDermott2019-10-191-2/+2
| | | | This should help with overhangs and bridges.
* eSUN HIPS, 3 mm: Unlimit fan speed (again)Patrick McDermott2019-10-191-2/+2
| | | | | | This was reverted in commit 6277ac681e24274f2cfd54af8270e596eb285f7c due to a crack between layers appearing, but cooling is needed for overhangs and bridges.
* Base: Reduce speeds to 20Patrick McDermott2019-10-191-10/+10
|
* Base: Reduce speeds to 40Patrick McDermott2019-10-191-8/+8
|
* Base: Reduce top, bottom, and bridge speeds to 60Patrick McDermott2019-10-191-5/+5
|
* Base: Reduce top, bottom, and bridge speeds to 80Patrick McDermott2019-10-191-4/+4
|
* Revert "eSUN HIPS, 3 mm: Raise temps"Patrick McDermott2019-10-191-5/+5
| | | | This reverts commit 0ffe3a57b1014f9519352a8f2a12d0089091e93e.
* eSUN HIPS, 3 mm: Raise tempsPatrick McDermott2019-10-191-5/+5
| | | | | A part 40 mm x 5 mm keeps lifting from the bed. With these changes it printed 25 mm up before lifting.
* Revert "Base: Slow down first layer"Patrick McDermott2019-10-191-2/+2
| | | | This reverts commit 2d7ef32ac94331723b33a9be93ea1ff5a71f8085.
* Base: Slow down first layerPatrick McDermott2019-10-191-2/+2
|
* Base: Set bridge speed to 100Patrick McDermott2019-10-191-2/+2
|
* Base: Raise perimeter and solid fill speeds to 100Patrick McDermott2019-10-191-6/+6
|
* Base: Decrease fill density to 10%Patrick McDermott2019-10-191-2/+2
|
* Base: Disable ineffective infill combinationPatrick McDermott2019-10-191-2/+2
| | | | Doesn't work when infill_every_layers * layer_height == nozzle_diameter.
* Revert "Base: Reduce layer height to 0.2 mm"Patrick McDermott2019-10-181-3/+3
| | | | | | | | This reverts commit ab84e54274cf87f575ff1436b064ac52df3f9ad9. The higher number of perimeter layers and lower number of infill layers almost balance each other out in print time. Layer seams are similar as well; if anything, the 0.2-mm seams protrude more.
* Base: Reduce layer height to 0.2 mmPatrick McDermott2019-10-181-3/+3
| | | | Now infill_every_layers is actually effective.
* Base: Raise perimeter and top infill speeds to 80Patrick McDermott2019-10-181-5/+5
|
* slic3r.ini: Switch to Base print settingsPatrick McDermott2019-10-181-1/+1
|
* Revert "eSUN HIPS, 3 mm: Unlimit fan speed"Patrick McDermott2019-10-181-2/+2
| | | | | | This reverts commit a37b85bc52468c7e4356f0922d2e970bed7a6aa6. That resulted in a crack.
* eSUN HIPS, 3 mm: Unlimit fan speedPatrick McDermott2019-10-181-2/+2
|
* eSUN HIPS, 3 mm: Lower extruder temps to 220Patrick McDermott2019-10-181-3/+3
|
* eSUN HIPS: Increase removal bed temp to 70Patrick McDermott2019-10-183-3/+3
|
* eSUN HIPS, 3 mm: Raise main bed temp to 100Patrick McDermott2019-10-181-2/+2
|
* eSUN HIPS, 3 mm: Lower extruder temp to 230Patrick McDermott2019-10-181-3/+3
|
* Revert "eSUN HIPS, 3 mm: Unlimit fan speed"Patrick McDermott2019-10-181-2/+2
| | | | | | | This reverts commit 08577e84f5bacc650dc5a2d19c428cea3666790c. This didn't fix the corner bulges. Instead, it restored shrinkage in the early layers after the first.
* eSUN HIPS, 3 mm: Unlimit fan speedPatrick McDermott2019-10-181-2/+2
| | | | This partially reverts commit 73981e3e924ad416ed38acadbd9cd75577ca2ec1.
* eSUN HIPS, 3 mm: Raise extruder temp to 240Patrick McDermott2019-10-181-2/+2
|
* Revert "eSUN HIPS, 3 mm: Raise bed temp to 100"Patrick McDermott2019-10-181-2/+2
| | | | This reverts commit 32c69f59df878f59fc8b3243ac4bd63b22d3022e.
* eSUN HIPS, 3 mm: Raise bed temp to 100Patrick McDermott2019-10-181-2/+2
| | | | Hoping to resolve minor warping.